1 – 2 of 2Murat Isik, Isa Emami Tabrizi, Raja Muhammad Awais Khan, Mehmet Yildiz, Eda Aydogan and Bahattin Koc
In recent years, additive manufacturing (AM) has started to be used for manufacturing real functional parts and assemblies for critical applications in aerospace, automotive, and…
Abstract
Purpose
In recent years, additive manufacturing (AM) has started to be used for manufacturing real functional parts and assemblies for critical applications in aerospace, automotive, and machinery industries. Most complex or assembled parts require internal features (IF) such as holes, channels, slots, or guides for locational and mating requirements. Therefore, it is critical to understand and compare the structural and mechanical properties of additively manufactured and conventionally machined IFs.
Design/methodology/approach
In this study, mechanical and microstructural properties of Inconel 718 (Inc718) alloy internal features, manufactured either as-built with AM or machining of additively manufactured (AMed) part thereafter were investigated.
Findings
The results showed that the average ultimate tensile strength (UTS) of additively manufactured center internal feature (AM-IF) is almost analogous to the machined internal feature (M-IF). However, the yield strength of M-IF is greater than that of AM-IF due the greater surface roughness of the internal feature in AM-IF, which is deemed to surpass the effect of microstructure on the mechanical performance. The results of digital image correlation (DIC) analysis suggest that AM-IF and M-IF conditions have similar strain values under the same stress levels but the specimens with as built IF have a more locally ductile region around their IF, which is confirmed by hardness test results. But this does not change global elongation behavior. The microstructural evolution starting from as-built (AB) and heat-treated (HT) samples to specimens with IF are examined. The microstructure of HT specimens has bimodal grain structure with d phase while the AB specimens display a very fine dendritic microstructure with the presence of carbides. Although they both have close values, machined specimens have a higher frequency of finer grains based on SEM images.
Originality/value
It was shown that the concurrent creation of the IF during AM can provide a final part with a preserved ultimate tensile strength and elongation but a decreased yield strength. The variation in UTS of AM-IF increases due to the surface roughness near the internal feature as compared to smooth internal surfaces in M-IF. Hence, the outcomes of this study are believed to be valuable for the industry in terms of determining the appropriate production strategy of parts with IF using AM and postprocessing processes.
Details
Keywords
Dhananjay A. Patil, Vidhukrishnan Ekambaram Naiker, Ganesh A. Phalak, Karan W. Chugh and S.T. Mhaske
This study aims to synthesize two different benzoxazines (Bz) monomers using bio-based and petroleum-based primary amines, respectively, and they have been compared to study their…
Abstract
Purpose
This study aims to synthesize two different benzoxazines (Bz) monomers using bio-based and petroleum-based primary amines, respectively, and they have been compared to study their thermal and mechanical performances.
Design/methodology/approach
A bio-based bisphenol, Divanillin (DiVa), was formed by reacting two moles of vanillin with one mole of ethylenediamine (EDA) which was then reacted firstly with paraformaldehyde and EDA to form the benzoxazine DiVa-EDA-Bz, and secondly with paraformaldehyde and furfuryl amine (FFA) to form the benzoxazine DiVa-FFA-Bz. The molecular structure and thermal properties of the benzoxazines were characterized by fourier transform infrared spectroscopy and nuclear magnetic resonance (1H,13C) spectroscopies, differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA), respectively. The benzoxazines were further coated on mild steel panels to evaluate their mechanical properties and chemical resistance.
Findings
The DSC results of DiVa-FFA-Bz showed two exothermic peaks related to crosslinking compared to the one in DiVa-EDA-Bz. The DiVa-FFA-Bz also showed a higher heat of polymerization than DiVa-EDA-Bz. The TGA results showed that DiVa-FFA-Bz exhibited higher thermal stability with a residual char of 54.10% than 43.24% for DiVa-EDA-Bz. The chemical resistance test results showed that DiVa-FFA-Bz showed better chemical resistance and mechanical properties due to its higher crosslinking density.
Originality/value
This study shows the use of bio-based materials, vanillin and FFA, for synthesizing a benzoxazine resin and its application at high temperatures.